Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials
Published on: January 10, 2025
In vitro evaluation of the color stability and surface roughness of a new composite flow
Gina Khazaal1, Maha Daou2, Syed-Sarosh Mahdi3,4,5
1Department of Esthetic and Prosthetic Dentistry, Dental Faculty, Saint Joseph University of Beirut, Lebanon.
Background:
The aim of this study was to evaluate the color stability and the surface roughness of a bulk-fill composite flow (SDR® Plus) by comparison to an ORMOCER-based composite (Ceram.x® Universal SphereTEC™) in order to confirm the validity of using SDR® Plus in the anterior region and to allow the prediction of its long-term results.
Material And Methods:
35 composite specimens of the same shade (A2), thickness (2mm) and shape of both types of composite were prepared. The specimens were cured and polished according to the manufacturer's instructions. The initial shade of the specimens was measured using a calibrated EasyShade spectrophotometer. The initial surface roughness of the specimens was measured by AFM. Afterwards, the specimens were subjected to an accelerated aging procedure through thermo-cycling, a coffee stain challenge and brushing to simulate two years in the oral environment. The shade and surface roughness of the specimens were measured again after the accelerated aging procedure.
Results:
The mean ΔE was significantly larger than 3.368 in Ceram.x® group (-p-value<0.001) and SDR® Plus group (-p-value<0.001). The mean surface roughness has significantly increased for both groups after aging with no significant difference between the two groups. It however remained clinically acceptable.
Conclusions:
SDR® Plus and Ceram.x® showed similar surface roughness when subjected to the same testing conditions. Concerning the color stability, both composites displayed noticeable discoloration, with higher ΔE values registered for Ceram.x®. Key words:Composite resins, spectrophotometry, atomic force microscopy, dental material, resin-based material.