Structural, Vibrational, and Magnetic Characterization of Orthoferrite LaFeO₃ Ceramic Prepared by Reaction Flash...

LaFeO₃ perovskite ceramics have been prepared via reaction flash technique using Fe₂O₃ and La₂O₃ as precursors. The obtained pellets have been investigated using several techniques. The formation of LaFeO₃ has been clearly confirmed by X-ray diffraction. The scanning electron microscopy micrographs have shown the microporous character of the obtained pellets due to the low temperature and dwell time used in the synthesis process (10 min at 1173 K). The orthorhombic-rhombohedral phase transition has been observed at approximately 1273 K in differential thermal analysis measurements, which also allows us to determine the Néel temperature at 742 K. The fitted Mössbauer spectra exposed the presence of a single sextet ascribed to the Fe⁺³ ions in the tetrahedral site. Finally, magnetic measurements at room temperature indicate the antiferromagnetic character of the sample.