Photocrosslinked Fish Collagen Peptide/Chitin Nanofiber Composite Hydrogels from Marine Resources: Preparation,
Shinya Yano1, Kei Yamaguchi1, Mitsuhiro Shibata1
1Department of Applied Chemistry, Faculty of Engineering, Chiba Institute of Technology, 2-17-1 Tsudanuma, Narashino, Chiba 275-0016, Japan.
Abstract:
Fish collagen peptide (FCP) is a water-soluble polymer with easy accessibility, bioactivity, and reactivity due to its solubility. The gelation of FCP can be carried out by chemical crosslinking, but the mechanical strength of FCP hydrogel is very low because of its intrinsically low molecular weight. Therefore, the mechanical properties of FCP gel should be improved for its wider application as a biomaterial. In this study, we investigated the mechanical properties of M-FCP gel in the context of understanding the influence of chitin nanofibers (CHNFs) on FCP hydrogels. FCP with a number average molecular weight (Mn) of ca. 5000 was reacted with glycidyl methacrylate (GMA) and used for the preparation of photocrosslinked hydrogels. Subsequently, composite hydrogels of methacrylate-modified FCP (M-FCP) and CHNF were prepared by the photoirradiation of a solution of M-FCP containing dispersed CHNF at an intensity of ~60 mW/cm2 for 450 s in the presence of 2-hydroxy-1-[4-(hydroxyethoxy)phenyl]-2-methyl-1-propanone (Irgacure 2959) as a photoinitiator. Compression and tensile tests of the FCP hydrogels were carried out using a universal tester. The compression and tensile strength of the hydrogel increased 10-fold and 4-fold, respectively, by the addition of 0.6% CHNF (20% M-FCP), and Young's modulus increased 2.5-fold (20% M-FCP). The highest compression strength of the M-FCP/CHNF hydrogel was ~300 kPa. Cell proliferation tests using fibroblast cells revealed that the hydrogel with CHNF showed good cell compatibility. The cells showed good adhesion on the M-FCP gel with CHNF, and the growth of fibroblast cells after 7 days was higher on the M-FCP/CHNF gel than on the M-FCP gel without CHNF. In conclusion, we found that CHNF improved the mechanical properties as well as the fibroblast cell compatibility, indicating that M-FCP hydrogels reinforced with CHNF are useful as scaffolds and wound-dressing materials.