In-situ release and sequestration of CO₂ in cement composites using LTA zeolites

This paper investigates the impact of in-situ release and sequestration of CO₂ on the compressive strength, volume of permeable voids, phase change, hydration reaction, and micro-morphology of cement mortars. Two Linde Type A (LTA) zeolites with micro-pore dimensions of 5 Å and 4 Å (i.e., LTA 5A and 4A zeolites) were employed as CO₂ carriers herein. The incorporation of 312 wt% plain LTA 5A and 4A zeolites increases the 1-day compressive strength of the mortars. However, the use of plain LTA 5A zeolite shows marginal contributions to the 7 and 28-day compressive strengths of the mortars, whilst using plain LTA 4A zeolite even deteriorates their 7 and 28-day compressive strengths. The micro-structural analyses reveal that the addition of LTA zeolites promotes the cement hydration and improves the mean chain length (MCL) of calcium aluminosilicate hydrates (C-A-S-H). Nevertheless, this introduces numerous weak points or even a porous structure to the cement matrix. In contrast, in-situ release of CO₂ via LTA zeolites significantly enhances the compressive strengths of the mortars at various ages, as this can further facilitate the hydration evolution and improve the MCL of C-A-S-H. Moreover, in-situ release of CO₂ brings an incremental content of calcium carbonates. The calcium carbonate contents in the specimens containing 12 wt% LTA 5A and 4A zeolites are increased by 5.3 wt% and 4.8 wt%, respectively. This leads to homogenous distributions of calcite with a grain size of 150600 nm. Thus, LTA 5A zeolite outperforms LTA 4A zeolite with regard to CO₂ uptake and the corresponding mechanical properties. This work presents in initial exploration into the application of porous pozzolanic materials in conjunction of CO₂ in cement-based materials.