Improved Performance of All-Inorganic Perovskite Light-emitting Diodes via Nanostructured Stamp Imprinting

Halide perovskites are emerging emitters with excellent optoelectronic properties. Contrary to the large grain fabrication goal in perovskite solar cells, perovskite light-emitting diodes (PeLEDs) based on small grain enable efficient radiative recombination because of relatively higher charge carrier densities due to spatial confinement. However, achieving small-sized grain growth with superior crystal quality and film morphology remains a challenge. In this work, we demonstrated a nanostructured stamp thermal imprinting strategy to boost the surface coverage and improve the crystalline quality of CsPbBr₃ film, particularly confine the grain size, leading to the improvement of luminance and efficiency of PeLEDs. We improved the thermal imprinting process utilizing the nanostructured stamp to selectively manipulate the nucleation and growth in the nanoscale region and acquire small-sized grain accompanied by improved crystal quality and surface morphology of the film. By optimizing the imprinting pressure and the period of the nanostructures, appropriate grain size, high surface coverage, small surface roughness and improved crystallization could be achieved synchronously. Finally, the maximum luminance and efficiency of PeLEDs achieved by nanostructured stamp imprinting with a period of 320 nm are 67600 cd/m² and 16.36 cd/A, respectively. This corresponds to improvements of 123 % in luminance and 100 % in efficiency, compared to that of PeLEDs without the imprinting.