Gas sensors based on the oxide skin of liquid indium

Various non-stratified two-dimensional (2D) materials can be obtained from liquid metal surfaces that are not naturally accessible. Homogenous nucleation on atomically flat interfaces of liquid metals with air produces unprecedented high-quality oxide layers that can be transferred onto desired substrates. The atomically flat and large areas provide large surface-to-volume ratios ideal for sensing applications. Versatile crucial applications of the liquid metal-derived 2D oxides have been realized; however, their gas-sensing properties remain largely underexplored. The cubic In₂O₃ structure, which is nonlayered, can be formed as an ultrathin layer on the surface of liquid indium during the self-limiting Cabrera-Mott oxidation process in the air. The morphology, crystal structure, and band structure of the harvested 2D In₂O₃ nanosheets from liquid indium are characterized. Sensing capability toward several gases, both inorganic and organic, entailing NO₂, O₂, NH₃, H₂, H₂S, CO, and Methyl ethyl ketone (MEK) are explored. A high ohmic resistance change of 1974% at 10 ppm, fast response, and recovery times are observed for NO₂ at an optimum temperature of 200 °C. The sensing fundamentals are investigated for NO₂, and its performances and cross-selectivity to different gases are analyzed. The NO₂ sensing response from room temperature to 300 °C has been measured and discussed, and stability after 24 hours of continuous operation is presented. The results demonstrate liquid metal-derived 2D oxides as promising materials for gas sensing applications.