The Fluoride Ion Release from Ion-Releasing Dental Materials after Surface Loading by Topical Treatment with Sodium...

The study aimed to investigate the rechargeability of ion-releasing dental material specimens immersed in distilled water for 25 months, which depleted their ion-releasing ability. Four restorative dental materials (alkasite composite, giomer, glass-ionomer, and composite material) presented with 24 specimens were studied after topical treatment with a concentrated fluoride gel. The effect of resin coating on the ion uptake and release was investigated on additional 42 specimens of restorative dental materials with coatings. The composite materials were coated with two adhesive systems, whereas the glass-ionomer was coated with the special coating resin. After topical fluoride exposure, ion release and specimen mass were measured at 1, 2, 3, 4, 5, 6, 7, and 14-day intervals using an ion-selective electrode and an analytical balance, respectively. The cumulative fluoride levels for the uncoated specimens of alkasite composite were significantly higher than those of giomer and glass-ionomer cement, with no statistically significant difference between the latter two materials. The conventional composite had the lowest cumulative concentration of fluoride ions (p < 0.05). The adhesive systems affected the fluoride recharge and reduced the ion concentrations absorbed by the specimens. Specimens coated with universal adhesive showed significantly higher ion release compared to universal fluoride-releasing adhesive or special coating resin for glass-ionomers (p < 0.05). No statistically significant change in specimen mass was observed during the 14-day period. Surface coating with adhesive systems as well as special coating resin for glass-ionomers affects the fluoride recharge process.