Synthesis and Crystal Structure of the Zintl Phases NaSrSb, NaBaSb and NaEuSb

This work details the synthesis and the crystal structures of the ternary compounds NaSrSb, NaBaSb and NaEuSb. They are isostructural and adopt the hexagonal ZrNiAl-type structure (space group P6¯2m; Pearson code hP9). The structure determination in all three cases was performed using single-crystal X-ray diffraction methods. The structure features isolated Sb^3- anions arranged in layers stacked along the crystallographic c-axis. In the interstices, alkali and alkaline-earth metal cations are found in tetrahedral and square pyramidal coordination environments, respectively. The formal partitioning of the valence electrons adheres to the valence rules, i.e., Na⁺Sr²⁺Sb^3-, Na⁺Ba²⁺Sb^3- and Na⁺Eu²⁺Sb^3- can be considered as Zintl phases with intrinsic semiconductor behavior. Electronic band structure calculations conducted for NaBaSb are consistent with this notion and show a direct gap of approx. 0.9 eV. Additionally, the calculations hint at possible inverted Dirac cones, a feature that is reminiscent of topological quantum materials.