Processing of Low-Density HGM-Filled Epoxy-Syntactic Foam Composites with High Specific Properties for Marine...

A solution casting approach is used to create hollow glass microsphere (HGM)-filled epoxy-syntactic foam composites (e-SFCs) by varying the concentrations of HGM in epoxy according to different particle sizes. Density analysis is used to investigate the impact of concentration and particle size regularity on the microstructure of e-SFCs. It was observed that e-SFCs filled with an HGM of uniform particle sizes exhibit a reduction in density with increasing HGM concentration, whereas e-SFCs filled with heterogeneous sizes of HGM exhibit closeness in density values regardless of HGM concentration. The variation in e-SFC density can be related to HGM packing efficiency within e-SFCs in terms of concentration and particle size regularity. The particle size with lowest true density of 0.5529 g/cm³, experimental density of 0.949 g/cm³ and tensile strength of 55.74 MPa resulted in e-SFCs with highest specific properties of 100.81 (MPa·g/cm³), with a 35.1% increase from the lowest value of 74.64 (MPa·g/cm³) at a true density of 0.7286 g/cm³, experimental density of 0.928 g/cm³ and tensile strength of 54.38 MPa. The e-SFCs' theoretical density values were obtained. The variance in theoretical and experimental density values provides a thorough grasp of packing efficiency and inter-particle features.