Preparation of Micro-Size Spherical Silver Particles and Their Application in Conductive Silver Paste

In this paper, micro-size spherical silver particles were prepared by using a wet-chemical reduction method. The silver particles were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and a laser particle-size analyzer. The results indicate that different types and the content of surfactants can be used to prevent the accumulation, and control the morphology and particle size distribution, of silver particles. Moreover, the morphology of silver particles was changed from polyhedral to spherical when the pH was raised from 1 to 3. Under the optimal synthesis conditions (0.1 mol/L silver nitrate, 0.06 mol/L ascorbic acid, gelatin (5% by weight of silver nitrate), pH = 1), the micro-size spherical silver particles with diameter of 5-8 μm were obtained. In addition, the resistivity of conductive silver paste that prepared with the as-synthesized spherical silver particles was discussed in detail and the average resistivity of the conductive silver paste was 3.57 × 10^-5 Ω·cm after sintering at 140 °C for 30 min.