Design of Liquid Crystal Materials Based on Palmitate, Oleate, and Linoleate Derivatives for Optoelectronic...

Herein, liquid crystalline derivatives based on palmitate, oleate, and linoleate moieties with azomethine cores were synthesized, and their physical, chemical, optical, and photophysical properties were investigated in detail. The mesomorphic activity of these materials was examined through polarized optical microscopy (POM) and differential scanning calorimetry (DSC). The observed results revealed that the stability of the thermal mesophase depends on the terminal polar as well as on the fatty long-chain substituents. Purely smectogenic phases were detected in all three terminal side chains. A eutectic composition with a low melting temperature and a broad smectic A range was found by constructing a binary phase diagram and addressing it in terms of the mesomorphic temperature range. The energy bandgap of the palmitate-based derivative (Ia) was determined as 3.95 eV and slightly increased to 4.01 eV and 4.05 eV for the oleate (Ib) and linoleate (Ic) derivatives, respectively. The optical constants (n, κ, ε_r, and ε_i) were extracted from the fitting of measured spectroscopic ellipsometer data. The steady-state spectra of these samples exhibited a broad emission in the range 400-580 nm, which was found to be blue shifted to 462 nm for both Ib and Ic derivatives. The average fluorescence decay lifetime of the Ia derivative was found to be 598 ps, which became faster for the Ib and Ic derivatives and slower for the sample with a chloride end polar group.