The Effect of Pre-Stretched Substrate on the Electrical Resistance of Printed Ag Nanowires

One-dimensional nanomaterials have drawn attention as an alternative electrode material for stretchable electronics. In particular, silver nanowires (Ag NWs) have been studied as stretchable electrodes for strain sensors, 3D electronics, and freeform-shaped electronic circuits. In this study, Ag NWs ink was printed on the pre-stretched silicone rubber film up to 40% in length using a drop-on-demand dispenser. After printing, silicone rubber film was released and stretched up to 20% as a cyclic test with 10-time repetition, and the ratios of the resistance of the stretched state to that of the released state (R_stretched/R_released) were measured at each cycle. For Ag NWs electrode printed on the pre-stretched silicone rubber at 30%, R_stretched/R_released at 10% and 20% strain was 1.05, and 1.57, respectively, which is significantly less than about 7 for Ag NWs at the 10% strain without pre-stretched substrate. In the case of 10% strain on the 30% pre-stretched substrate, the substrate is stretched and the contact points with Ag NWs were not changed much as the silicone rubber film stretched, which meant that Ag NWs may slide between other Ag NWs. Ag NWs electrode on the 40% pre-stretched substrate was stretched, strain was concentrated on the Ag NWs electrode and failure of electrode occurred, because cracks occurred at the surface of silicone rubber film when it was pre-stretched to 40%. We confirmed that printed Ag NWs on the pre-stretched film showed more contact points and less electric resistance compared to printed Ag NWs on the film without pre-stretching.