Waste lignin-based cationic flocculants treating dyeing wastewater: Fabrication, performance, and mechanism

Lignin is often considered to be a complex polymeric structural material with excellent scalability. Reduced pressure distillation, a novel effective way, was proposed to recover reusable waste lignin from textile degumming black liquor. The structure of the recovered material was determined by Fourier Transform Infrared Spectroscopy (FT-IR), Gel Permeation Chromatography (GPC) and Klason Component Analysis. Recycled lignin (RL) was used as the basis for the synthesis of a cationic recycled lignin-based polymers (CRLM) through graft polymerizing cationic monomer (DMC). The optimum synthesis conditions were obtained by conducting orthogonal experiments using the cationicity as the studied parameter, while selecting pH, DMC/RL, reaction temperature and time as independent variables. Recovery experiments showed that the maximum recovery concentration of RL in the black liquor was 5 g/L, with a purity of approximately 83 %. Orthogonal experiments showed that a low DMC/RL ratio was crucial for the synthesis of flocculants. When the molar ratio of DMC/RL was 3:1, the cationicity of the prepared CRLM was as high as 11.32 %. Zeta potential and decolorization experiments also confirmed the stable decolorization performance of CRLM in three kinds of anionic dye wastewater. The experimental results showed that charge neutralization, chemical bonding forces and auxiliary effects play great role to remove anionic dyes, resulting in 94 %, 89 % and 94.9 % removal against Reactive Red 195 (RR195), Acid Red 18 (AR18) and Direct 168 (DB168) respectively. Therefore, this study demonstrated the potential of using recycled waste lignin as synthesize lignin-based flocculants in the field of printing and dyeing wastewater by treating waste with waste.