Microfibrillated Cellulose with a Lower Degree of Polymerization; Synthesis via Sulfuric Acid Hydrolysis under Ultrasonic Treatment
Yuriy N Malyar1,2, Irina G Sudakova1, Valentina S Borovkova1,2
1Institute of Chemistry and Chemical Technology, Krasnoyarsk Science Center, Siberian Branch Russian Academy of Sciences, Akademgorodok 50/24, Krasnoyarsk 660036, Russia.
Abstract:
A new approach is being considered for obtaining microfibrillated cellulose with a low degree of polymerization by sulfuric acid hydrolysis with simultaneous ultrasonic treatment under mild conditions (temperature 25 °C, 80% power control). Samples of initial cellulose, MCC, and MFC were characterized by FTIR, XRF, SEM, DLS, and TGA. It was found that a high yield of MFC (86.4 wt.%) and a low SP (94) are observed during hydrolysis with ultrasonic treatment for 90 min. It was shown that the resulting microfibrillated cellulose retains the structure of cellulose I and has an IC of 0.74. It was found that MFC particles are a network of fibrils with an average size of 91.2 nm. ζ-potential of an aqueous suspension of MFC equal to -23.3 mV indicates its high stability. It is noted that MFC has high thermal stability, the maximum decomposition temperature is 333.9 °C. Simultaneous hydrolysis process with ultrasonic treatment to isolate MFC from cellulose obtained by oxidative delignification of spruce wood allows to reduce the number of stages, reduce energy costs, and expand the scope.