Effectiveness of Surface Treatment on Bonding Performance of Starch-Based Aqueous Polymer Isocyanate Wood Adhesive

The surface of a bonding material plays a key role in the bonding performance of an adhesive. Herein, we evaluated the effect of substrate surface treatment methods (sandpaper polished, chemical oxidation, and coupling agent) on the adhesive properties of starch-based aqueous polymer isocyanate (API) wood adhesive during hygrothermal aging. The birch substrate was processed with three different surface treatments, and the change of surface was analyzed by X-ray Photoelectron Spectroscopy (XPS), Fourier Transform Infrared spectroscopy (FT-IR), and Energy Dispersive Spectroscopy (EDS) methods. The results showed that the surface treatment had a great influence on the change of the shear strength of glued wood under hygrothermal conditions, and the silane coupling agent treatment could effectively reduce the decrease in the compressive shear strength of the adhesive. An XPS analysis indicated that the chemical oxidation modified wood surface polarity, and the coupling agent treatment in the wood surface formed a transition layer. After hygrothermal aging treatment, due to the different surface treatment of adhesive joint surface binding energy, the internal water absorption rate of starch-based API adhesives exhibited different failure modes of the adhesive joint. These findings indicate that the surface treatment effectively improved the durability of the adhesive joints.