Mussel-Inspired Robust Peony-like Cu₃(PO₄)₂ Composite Switchable Superhydrophobic Surfaces for Bidirectional...

To alleviate the economic and environmental damage caused by industrial discharges of oily wastewater, materials applied for efficient oil/water separation are receiving significant attention from researchers and engineers. Among others, switchable wettable materials for bidirectional oil/water separation show great potential for practical applications. Inspired by mussels, we utilized a simple immersion method to construct a polydopamine (PDA) coating on a peony-like copper phosphate surface. Then, TiO₂ was deposited on the PDA coating surface to build a micro-nano hierarchical structure, which was modified with octadecanethiol (ODT) to obtain a switchable wettable peony-like superhydrophobic surface. The water contact angle of the obtained superhydrophobic surface reached 153.5°, and the separation efficiency was as high as 99.84% with a flux greater than 15,100 L/(m²·h) after 10 separation cycles for a variety of heavy oil/water mixtures. Notably, the modified membranes have a unique photoresponsiveness, transforming to superhydrophilic upon ultraviolet irradiation, achieving separation efficiencies of up to 99.83% and separation fluxes greater than 32,200 L/(m²·h) after 10 separation cycles for a variety of light oil/water mixtures. More importantly, this switch behavior is reversible, and the high hydrophobicity can be restored after heating to achieve efficient separation of heavy oil/water mixtures. In addition, the prepared membranes can maintain high hydrophobicity under acid-base conditions and after 30 sandpaper abrasion cycles, and damaged membranes can be restored to superhydrophobicity after a brief modification in the ODT solution. This simple-to-prepare, easy-to-repair, robust membrane with switchable wettability shows great potential in the field of oil/water separation.