Development of chitosan/rice protein hydrolysates/ZnO nanoparticles films reinforced with cellulose nanocrystals

In the present work, the composite films were obtained by the solution casting method from chitosan and rice protein hydrolysates, reinforced with cellulose nanocrystals (CNC) of different contents (0 %, 3 %, 6 % and 9 %). The influence of different CNC loadings on the mechanical, barrier and thermal properties was discussed. SEM showed the formation of intramolecular interactions between the CNC and film matrices, leading to more compact and homogeneous films. These interactions had a positive influence on the mechanical strength properties, which was reflected in higher breaking force of 4.27 MPa. The elongation dwindled from 132.42 % to 79.37 % with increasing CNC levels. The linkages formed between the CNC and film matrices reduced the water affinity, leading to a reduction in their moisture content, water solubility and water vapor transmission. Thermal stability of the composite films was also improved in the presence of CNC, by increasing maximum degradation temperature from 311.21 to 325.67 °C with increasing CNC contents. The strongest DPPH inhibition of the film was 45.42 %. The composite films exhibited the highest inhibition zone diameter against E. coli (12.05 mm) and S. aureus (12.48 mm), and the hybrid of CNC and ZnO nanoparticles exhibited stronger antibacterial activity than their single existent forms. The present work shows the possibility of obtaining CNC-reinforced films with improved mechanical, thermal and barrier properties.