Fabricating Amorphous Zero-Valent Iron for Cr(VI) Efficient Reduction: Unveiling the Effect of Ethylenediamine on
Zishen Lin1, Fobang Liu1, Chunli Zheng1,2
1Department of Environmental Science and Engineering, Xi'an Jiaotong University, Xi'an 710049, P.R. China.
Abstract:
Amorphous zero-valent iron (AZVI) has attracted wide attention due to its high-efficiency reduction ability. However, the effect of different EDA/Fe(II) molar ratios on the physicochemical properties of the synthesized AZVI requires further investigation. Herein, series of AZVI samples were prepared by changing the molar ratio of EDA/Fe(II) to 1/1 (AZVI@1), 2/1 (AZVI@2), 3/1 (AZVI@3), and 4/1 (AZVI@4). When the EDA/Fe(II) ratio increased from 0/1 to 3/1, the Fe0 proportion on the AZVI surface increased from 26.0 to 35.2% and the reducing ability was enhanced. As for AZVI@4, the surface was severely oxidized to form a large amount of Fe3O4, and the Fe0 content was only 74.0%. Moreover, the removal ability of Cr(VI) was in the order AZVI@3 > AZVI@2 > AZVI@1 > AZVI@4. The isothermal titration calorimetry results revealed that the increase of the molar ratio of EDA/Fe(II) would lead to the stronger complexation of EDA with Fe(II), which resulted in the gradual decrease of the yield of AZVI@1 to AZVI@4 and the gradual deterioration of water pollution after the synthesis. Therefore, based on the evaluation of all indicators, AZVI@2 was the optimal material, not only because its yield was as high as 88.7% and the secondary water pollution level was low, but most importantly, the removal efficiency of Cr(VI) by AZVI@2 was excellent. Furthermore, the actual Cr(VI) wastewater with the concentration of 14.80 mg/L was treated with AZVI@2, and the removal rate of 97.0% was achieved after only a 30 min reaction. This work clarified the effect of different ratios of EDA/Fe(II) on the physicochemical properties of AZVI, which provided insights for guiding the reasonable synthesis of AZVI and is also conducive to investigating the reaction mechanism of AZVI in Cr(VI) remediation.
Related Concept Videos
02:24Reduction of Alkynes to cis-Alkenes: Catalytic Hydrogenation
Like alkenes, alkynes can be reduced to alkanes in the presence of transition metal catalysts such as Pt, Pd, or Ni. The reaction involves two sequential syn additions of hydrogen via a cis-alkene intermediate.
02:10Reduction of Alkynes to trans-Alkenes: Sodium in Liquid Ammonia
When dissolved in liquid ammonia, an alkali metal, such as sodium, dissociates into a...
01:20Amides to Amines: LiAlH4 Reduction
Amide reduction requires two equivalents of the reducing agent, acting as a source of hydride ions. As shown in the figure, the reaction is initiated with a nucleophilic attack by the hydride ion at the carbonyl carbon to form a tetrahedral intermediate.
00:55Nitriles to Amines: LiAlH4 Reduction
As shown below, the mechanism involves three steps. Firstly, the hydride ion acting as a nucleophile attacks the nitrile carbon to form an anion. In the second step, a second equivalent of the hydride ion attacks the anion to...