Nanoscale control and tri-element co-doping of 4.6 V LiCoO₂ with excellent rate capability and long-cycling stability...

Structural instability at high voltage severely restricts the reversible capacity of the LiCoO₂ cathode. Moreover, the main difficulties in achieving high-rate performance of LiCoO₂ are the long Li⁺ diffusion distance and slow Li⁺ intercalation/extraction during the cycle. Thus, we designed a modification strategy of nanosizing and tri-element co-doping to synergistically enhance the electrochemical performance of LiCoO₂ at high voltage (4.6 V). Mg, Al, and Ti co-doping maintains the structural stability and phase transition reversibility, which promotes the cycling performance of LiCoO₂. After 100 cycles at 1 C, the capacity retention of the modified LiCoO₂ reached 94.3%. In addition, the tri-elemental co-doping increases Li⁺ interlayer spacing and enhances Li⁺ diffusivity by tens of times. Simultaneously, nanosize modification decreases Li⁺ diffusion distance, leading to a significantly enhanced rate capacity of 132 mA h g^-1 at 10 C, much better than that of the unmodified LiCoO₂ (2 mA h g^-1). After 600 cycles at 5 C, the specific capacity remains at 135 mA h g^-1 with a capacity retention of 91%. The nanosizing co-doping strategy synchronously enhanced the rate capability and cycling performance of LiCoO₂.