Solution-Processed Large-Area Organic/Inorganic Hybrid Antireflective Films for Perovskite Solar Cell

In recent years, organic/inorganic hybrid materials have attracted much attention in the field of multilayer antireflection films because of their excellent optical properties. In this paper, the organic/inorganic nanocomposite was prepared from polyvinyl alcohol (PVA) and titanium (IV) isopropoxide (TTIP). The hybrid material has a wide, tunable window of refractive index, i.e., 1.65-1.95, at a wavelength of 550 nm. The atomic force microscope (AFM) results of the hybrid films show the lowest root-mean-square surface roughness of 2.7 Å and a low haze of 0.23%, indicating that the films have good potential for optical applications. The double-sided antireflection films (10 × 10 cm²) with one side of hybrid nanocomposite/cellulose acetate and the other side of hybrid nanocomposite /polymethyl methacrylate (PMMA) achieved high transmittances of 98% and 99.3%, respectively. After 240 days of aging testing, the hybrid solution and the antireflective film remained stable with almost no attenuation. Furthermore, the application of the antireflection films in perovskite solar cell modules increased the power conversion efficiency from 16.57% to 17.25%.