PET/Graphene Nanocomposite Fibers Obtained by Dry-Jet Wet-Spinning for Conductive Textiles

The combination of polyethylene terephthalate (PET), one of the most used polymers in the textile industry, with graphene, one of the most outstanding conductive materials in recent years, represents a promising strategy for the preparation of conductive textiles. This study focuses on the preparation of mechanically stable and conductive polymer textiles and describes the preparation of PET/graphene fibers by the dry-jet wet-spinning method from nanocomposite solutions in trifluoroacetic acid. Nanoindentation results show that the addition of a small amount of graphene (2 wt.%) to the glassy PET fibers produces a significant modulus and hardness enhancement (≈10%) that can be partly attributed to the intrinsic mechanical properties of graphene but also to the promotion of crystallinity. Higher graphene loadings up to 5 wt.% are found to produce additional mechanical improvements up to ≈20% that can be merely attributed to the superior properties of the filler. Moreover, the nanocomposite fibers display an electrical conductivity percolation threshold over 2 wt.% approaching ≈0.2 S/cm for the largest graphene loading. Finally, bending tests on the nanocomposite fibers show that the good electrical conductivity can be preserved under cyclic mechanical loading.