Quaternized Poly(N,N'-dimethylaminoethyl methacrylate) Star Nanostructures in the Solution and on the Surface

Antibacterial polymeric materials are promising in the fight against resistant bacteria strains. Amongst them, cationic macromolecules with quaternary ammonium groups are one of intensively studied, as they interact with the bacterial membranes causing cell death. In this work, we propose to use nanostructures composed of polycations with star topology for the preparation of antibacterial materials. First, star polymers of N,N'-dimethylaminoethyl methacrylate and hydroxyl-bearing oligo(ethylene glycol) methacrylate P(DMAEMA-co-OEGMA-OH) were quaternized with various bromoalkanes and their solution behavior was studied. It was shown that in water two modes of star nanoparticles were observed, of diameters about 30 nm and up to 125 nm, independently of the quaternizing agent. Separately layers of P(DMAEMA-co-OEGMA-OH) stars were obtained. In this case, the chemical grafting of polymers to the silicon wafers modified with imidazole derivatives was applied, followed by the quaternization of the amino groups of polycations. A comparison of the quaternary reaction in solution and on the surface showed that in the solution it is influenced by the alkyl chain length of the quaternary agent, while on the surface such relationship is not observed. After physico-chemical characterization of the obtained nanolayers, their biocidal activity was tested against two strains of bacteria E. coli and B. subtilis. The best antibacterial properties exhibited layers quaternized with shorter alkyl bromide, where 100% growth inhibition of E. coli and B. subtilis after 24 h of contact was observed.