Mechanical characterization of miniaturized 3D-printed hydroxyapatite parts obtained through vat photopolymerization:...

Hydroxyapatite is one of the materials of choice for tissue engineering bone scaffolds manufacturing. Vat photopolymerization (VPP) is a promising Additive Manufacturing (AM) technology capable of producing scaffolds with high resolution micro-architecture and complex shapes. However, mechanical reliability of ceramic scaffolds can be achieved if a high fidelity printing process is obtained and if knowledge of the intrinsic mechanical properties of the constituent material is available. As the hydroxyapatite (HAP) obtained from VPP is subjected to a sintering process, the mechanical properties of the material should be assessed with specific reference to the process parameters (e.g. sintering temperature) and to the specific characteristic size of the microscopic features in the scaffolds. In order to tackle this challenge the HAP solid matrix of the scaffold was mimicked in the form of miniaturized samples suitable for ad hoc mechanical characterization, which is an unprecedented approach. To this purpose small scale HAP samples, having a simple geometry and size similar to that of the scaffolds, were produced through VPP. The samples were subjected to geometric characterization and to mechanical laboratory tests. Confocal laser scanning and Computed micro-Tomography (micro-CT) were used for geometric characterization; while, micro-bending and nanoindentation were used for mechanical testing. Micro-CT analyses have shown a highly dense material with negligible intrinsic micro-porosity. The imaging process allowed quantifying the variation of geometry with respect to the nominal size showing high accuracy of the printing process and identifying printing defects on one specific sample type, depending on the printing direction. The mechanical tests have shown that the VPP produces HAP with an elastic modulus as high as approximately 100GPa and flexural strength of approximately 100MPa. The results of this study have shown that vat photopolymerization is a promising technology capable of producing high quality HAP with reliable geometric fidelity.