Cobalt-Carbon nanotubes supported on V₂O₃ nanorods as sulfur hosts for High-performance Lithium-Sulfur batteries

Exploring advanced sulfur cathode materials with high catalytic activity to accelerate the slow redox reactions of lithium polysulfides (LiPSs) is of great significance for lithium-sulfur batteries (LSBs). In this study, a coral-like hybrid composed of cobalt nanoparticle-embedded N-doped carbon nanotubes supported by Vanadium (III) oxide (V₂O₃) nanorods (Co-CNTs/C @V₂O₃) was designed as an efficient sulfur host using a simple annealing process. Characterization combined with electrochemical analysis confirmed that the V₂O₃ nanorods exhibited enhanced LiPSs adsorption capacity, and the in situ grown short-length Co-CNTs improved electron/mass transport and enhanced the catalytic activity for conversion to LiPSs. Owing to these merits, the S@Co-CNTs/C@V₂O₃ cathode exhibits effective capacity and cycle lifetime. Its initial capacity was 864 mAh g^-1 at 1.0C and remained at 594 mAh g^-1 after 800cycles with a decay rate of 0.039%. Furthermore, even at a high sulfur loading (4.5 mg cm^-2), S@Co-CNTs/C@V₂O₃ also shows acceptable initial capacity of 880 mAh g^-1 at 0.5C. This study provides new ideas for preparing long-cycle S-hosting cathodes for LSBs.