Texture and Magnetic Property of Fe-6.5 wt % Si Steel Strip with Cu-Rich Particles Modification

Based on the ordered phase effectively suppressed by rapid solidification technology, the grain refinement concept using Cu is incorporated into the soft magnetic materials. Cu dosage not only could refine the grain size with an average grain size of 8.7 μm but also improve the continuity and consistency of Fe-6.5 wt % Si steel strip. It mainly attributes to the Cu-rich particles precipitating at the grain boundary, nailing the grain boundaries movement and inhibiting the grain growth, and then improving the magnetic properties and mechanical properties. The 1.5 wt % Cu sample exhibits an excellent magnetic property with the saturation magnetization of 236.54 emu/g, which mainly attributes to the strong η, λ, Goss texture formation and the band structure optimization of Si-Cu comodification. Furthermore, the mechanical properties of the steel strip are effectively improved, and the failure plastic deformation of 1.5 wt % Cu steel strip is about 11%. The rapid solidification with Cu-dosage refinement technology also has a remarkable reference on the mechanical properties and magnetic properties modification of other metal materials.