Repair Bond Strength to Hybrid CAD/CAM Materials after Silane Heat Treatment with Laser

This study investigated the effect of different surface treatments and the effect of silane heat treatment with laser on the shear bond strength (SBS) of a nanoceramic composite to repaired hybrid CAD/CAM blocks.

60 hybrid CAD/CAM specimens (Cerasmart, GC) were prepared and randomly divided into six groups according to the different surface treatments (n = 10): group ER: Er:YAG laser+silane (Monobond Plus, Ivoclar Vivadent); group ER+SHT: Er:YAG laser+silane heat treatment; group B: bur+silane; group B+SHT: bur+silane heat treatment; group HF: hydrofluoric acid+silane; group HF+SHT: hydrofluoric acid+silane heat treatment. Afterwards, a universal adhesive (Universal Bond Quick, Kuraray) was applied, and nanoceramic resin composite (Zenit, President) cylinders were bonded to the Cerasmart specimens. They were thermocycled for 10,000 cycles (5-55°C) and subjected to SBS testing using a universal testing machine. Failure modes were examined with a stereomicroscope (15X). Scanning electron microscopy (SEM) was used to evaluate the surface topography (n = 2). The data were statistically analyzed using the Mann-Whitney U-test and the Kruskal-Wallis test (p < 0.05).

Regarding the surface treatments, group ER showed significantly lower SBS than groups B and HF (p < 0.05). Regarding the presence of silane heat treatment by laser, groups ER+SHT and B+SHT showed significantly lower SBS than group HF+SHT(p < 0.05). In addition, group B+SHT showed significantly lower SBS than did group B (p < 0.05).

Er:YAG laser treatment for repairing hybrid CAD/CAM blocks was not as effective as bur roughening or hydrofluoric acid etching. Silane heated by Er:YAG laser was incapable of significantly increasing the bond strength to repaired hybrid CAD/CAM blocks.