Carbon nanotubes as a nitric oxide nano-reservoir improved the controlled release profile in 3D printed biodegradable...

Small diameter vascular grafts (SDVGs) are associated with a high failure rate due to poor endothelialization. The incorporation of a nitric oxide (NO) releasing system improves biocompatibility by using the NO effect to promote endothelial cell (EC) migration and proliferation while preventing bacterial infection. To circumvent the instability of NO donors and to prolong NO releasing, S-nitroso-N-acetyl-D-penicillamine (SNAP) as a NO donor was loaded in multi-walled carbon nanotubes (MWCNTs). Successful loading was confirmed with a maximum SNAP amount of ~ 5% (w/w) by TEM, CHNS analysis and FTIR spectra. SDVGs were 3D printed from polycaprolactone (PCL) and coated with a 1:1 ratio of polyethylene glycol and PCL dopped with different concentrations of SNAP-loaded matrix and combinations of MWCNTs-OH. Coating with 10% (w/w) SNAP-matrix-10% (w/w) SNAP-MWCNT-OH showed a diminished burst release and 18 days of NO release in the range of 0.5-4 × 10^-10 mol cm^-2 min^-1 similar to the NO release from healthy endothelium. NO-releasing SDVGs were cytocompatible, significantly enhanced EC proliferation and migration and diminished bacterial viability. The newly developed SNAP-loaded MWCNT-OH has a great potential to develop NO releasing biomaterials with a prolonged, controlled NO release promoting in-situ endothelialization and tissue integration in vivo, even as an approach towards personalized medicine.