Growth of single-crystal black phosphorus and its alloy films through sustained feedstock release

Black phosphorus (BP), a fascinating semiconductor with high mobility and a tunable direct bandgap, has emerged as a candidate beyond traditional silicon-based devices for next-generation electronics and optoelectronics. The ability to grow large-scale, high-quality BP films is a prerequisite for scalable integrated applications but has thus far remained a challenge due to unmanageable nucleation events. Here we develop a sustained feedstock release strategy to achieve subcentimetre-size single-crystal BP films by facilitating the lateral growth mode under a low nucleation rate. The as-grown single-crystal BP films exhibit high crystal quality, which brings excellent field-effect electrical properties and observation of pronounced Shubnikov-de Haas oscillations, with high mobilities up to ~6,500 cm² V^-1 s^-1 at low temperatures. We further extend this approach to the growth of single-crystal BP alloy films, which broaden the infrared emission regime of BP from 3.7 μm to 6.9 μm at room temperature. This work will greatly facilitate the development of high-performance electronics and optoelectronics based on BP family materials.