The effect of different concentrations of fluoride in toothpastes with or without bioactive glass on artificial root
Haoran Chen1, Robert Hill1, Aylin Baysan1
1Institute of Dentistry, Barts and The London School of Medicine and Dentistry, Queen Mary University of London, London, UK.
Objective:
To investigate the effect of different toothpastes either containing 5,000ppm-F, 1,450ppm-F or bioactive glass (BG) with 540ppm-F on artificial root carious lesions (ARCLs).
Method:
The crowns of 23 extracted sound teeth were removed leaving their roots only. Subsequently, each root was divided into four parts. A total of 15 sound root dentine (SRD) was left untreated as baseline. The ARCLs were developed for the remaining roots using demineralisation solution (pH-4.8). 15-ARCLs samples were then left untreated. The rest of samples were divided into four groups (n = 15 each) and treated with Group-1(BG with 540ppm-F); Group-2(5000ppm-F); Group-3(1450ppm-F) and Group-4(deionised water). 13-day pH-cycling included using demineralisation solution for 6 h, then placing samples into remineralisation solution (pH-7) for 16 h. Each sample was brushed with the assigned toothpaste twice a day during pH-cycling. Fluoride concentrations at each time point were measured using F-ISE, whilst calcium (Ca2+) and phosphorus (P) ion release was determined using ICP-OES, KHN, XRD, 19F-MAS-NMR analyses.
Results:
KHN showed significant surface changes for each group (p<0.001). The uptake of Ca2+ occurred at days 1-2, phosphorus ion loss was high when compared to the uptake in all groups. XRD showed presence of sharp diffraction lines evidencing apatite formation for Groups 1-3. 19F-MAS-NMR confirmed fluorapatite presence in Groups 1-3.
Conclusion:
All toothpastes were promising in fluorapatite formation. BG with 540ppm-F toothpaste released more ions (Ca2+and P) and reharden the artificial root carious lesions when compared to other groups. However, 1450ppm-F toothpaste showed more fluoride-substituted apatite formation whilst 5000ppm-F toothpaste had more fluorapatite formation.
Clinical Significance:
Toothpaste containing BG with 540ppm-F, 5000ppm-F and 1450ppm-F toothpastes are likely to have a significant impact in reversing and arresting root caries. However, randomised controlled double-blinded clinical trials are required to translate these results into clinical practice.