Hydrogel Based on Polyhydroxyalkanoate Sulfonate: Control of the Swelling Rate by the Ionic Group Content

Hydrogels based on poly(3-hydroxyalkanoate) (PHA) sulfonate and poly(ethylene glycol) diacrylate, PEGDA, are prepared. First, PHA sulfonate is synthesized from unsaturated PHA by a thiol-ene reaction in the presence of sodium-3-mercapto-1-ethanesulfonate. The hydrophilicity of PHAs is considerably increased by adding sulfonate functions, and three amphiphilic PHAs are synthesized, containing 10, 22, or 29% sulfonate functions. Then, hydrogels are formed in the presence of PEGDA having different molar masses, that is, 575 or 2000 g mol^-1. The hydrogels show fibrillar and porous structures observed in cryo-MEB with pore sizes that vary according to the content of sulfonated groups (10 to 29 mol %) ranging from 50 to more than 150 nm. Furthermore, depending on the proportions of the two polymers, a variable rigidity is observed from 2 to 40 Pa. In fact, the evaluation of the dynamic mechanical properties of the hydrogel determined by DMA reveals that the less rigid hydrogels hinder the adhesion of Pseudomonas aeruginosa PaO1 bacteria. Finally, these hydrogels swelling up to 5000% are noncytotoxic, allowing the adhesion and amplification of immortalized C2C12 cells, and they are therefore seen as promising materials both for repelling PaO1 bacteria and for amplifying myogenic cells.