Deterministic Magnetic Switching in Perpendicular Magnetic Trilayers Through Sunlight-Induced Photoelectron Injection

Finding an energy-efficient way of switching magnetization is crucial in spintronic devices, such as memories. Usually, spins are manipulated by spin-polarized currents or voltages in various ferromagnetic heterostructures; however, their energy consumption is relatively large. Here, a sunlight control of perpendicular magnetic anisotropy (PMA) in Pt (0.8 nm)/Co (0.65 nm)/Pt (2.5 nm)/PN Si heterojunction in an energy-efficient manner is proposed. The coercive field (H_C ) is altered from 261 to 95 Oe (64% variation) under sunlight illumination, enabling a nearly 180° deterministic magnetization switching reversibly with a 140 Oe magnetic bias assistant. The element-resolved X-ray circular dichroism measurement reveals different L3 and L2 edge signals of the Co layer with or without sunlight, suggesting a photoelectron-induced redistribution of the orbital and spin moment in Co magnetization. The first-principle calculations also reveal that the photo-induced electrons shift the Fermi level of electrons and enhance the in-plane Rashba field around the Co/Pt interfaces, leading to a weakened PMA and corresponding H_C decreasing and magnetization switching accordingly. The sunlight control of PMA may provide an alternative way for magnetic recording, which is energy efficient and would reduce the Joule heat from the high switching current.