Microstructural and Electrochemical Influence of Zn in MgCaZn Biodegradable Alloys

In recent years, biodegradable materials have included magnesium alloys with homogenous disintegration and a controllable degradation rate. Utilized in medical applications, biodegradable materials based on magnesium have been widely explored throughout the years. It is well-known that alloying Mg with biocompatible and non-toxic elements increases the biodegradability of surgical alloys. The purpose of this study was to examine the microstructure and the electrochemical response (corrosion resistance) of a new experimental Mg-based biodegradable alloy-Mg-0.5%Ca with additions of Zn as follows: 0.5, 1.5, and 3.0 wt.% in order to control the corrosion rate. Immersion tests were performed for different periods in a simulated body fluid electrolyte solution at 37 °C, and the mass loss was appreciated in order to calculate the corrosion rate (CR). The investigation led to the discovery of a dendritic Mg solid solution, a lamellar Mg₂Ca compound, and a MgZn₂ intermetallic phase. Scanning electron microscopy, optical microscopy, and energy dispersive spectroscopy were used for surface analysis after the immersion and electro-corrosion resistance tests. The metallic and ceramic compounds that detached themselves from the sample and passed into the solution were evaluated using the SEM-EDS system. All samples presented a generalized electro-corrosion with anodic and cathodic reactions of similar intensity. The corrosion rate was similar regardless of the percentage of zinc, with a smaller value for a higher than 3 wt.% Zn percentage based on the more protective zinc oxide that appeared on the surface.