Mechanical Properties under Compression and Microscopy Analysis of Basalt Fiber Reinforced Recycled Aggregate...

In this study, the basalt fiber content (0%, 0.075%, and 0.15%) and replacement ratio of recycled coarse aggregate (0%, 50%, and 100%) were used as parameters, and the compressive strength of 15 cubes and 15 prisms was analyzed. The failure morphology of the specimens was characterized, and the cubic compressive strength, axial compressive strength, elastic modulus, Poisson's ratio, and other mechanical property indices of the specimens were measured. Upon increasing the replacement ratio, the degree of damage of the specimens gradually increased, whereas the cubic compressive strength, axial compressive strength, and elastic modulus gradually decreased. As the replacement ratio was increased from 50% to 100%, the cubic compressive strength and elastic modulus were noted to decrease the most by about 9.07% and 9.87%, respectively. On the other hand, the Poisson's ratio first decreased, followed by an increase. Upon increasing the fiber content, the degree of damage of the specimens was gradually reduced, whereas the cubic compressive strength, axial compressive strength, and elastic modulus gradually increased. As the fiber content increased from 0.075% to 0.15%, the axial compressive strength and elastic modulus increased the most by about 6.65% and 10.19%, respectively. On the other hand, the Poisson's ratio gradually decreased. Based on the test data, the functional relationships between the strength indices and different variables, as well as the conversion value of each strength index and different variables were established; after comparison and verification, the formula calculation results were found to be in good agreement with the test results. The microstructural changes in the basalt fiber reinforced recycled aggregate concrete were characterized by scanning electron microscopy (SEM), and the changes in the mechanical properties of the basalt fiber reinforced recycled aggregate concrete as well as the mechanism of fiber modification and reinforcement were explained from a micro perspective.