Hydrophobically Associating Polyacrylamide "Water-in-Water" Emulsion Prepared by Aqueous Dispersion Polymerization:
Yongli Lv1, Sheng Zhang2, Yunshan Zhang2
1Petroleum Engineering Technology Research Institute of Shengli Oilfield, SINOPEC, Dongying 257000, China.
Abstract:
The hydrophobically associating polyacrylamide (HAPAM) is an important kind of water-soluble polymer, which is widely used as a rheology modifier in many fields. However, HAPAM products prepared in a traditional method show disadvantages including poor water solubility and the need for hydrocarbon solvents and appropriate surfactants, which lead to environmental pollution and increased costs. To solve these problems, we reported a novel kind of HAPAM "water-in-water" (w/w) emulsion and its solution properties. In this work, a series of cationic hydrophobic monomers with different alkyl chain lengths were synthesized and characterized. Then, HAPAM w/w emulsions were prepared by the aqueous dispersion polymerization of acrylamide, 2-methylacryloylxyethyl trimethyl ammonium chloride and a hydrophobic monomer. All these emulsions can be stored more than 6 months, showing excellent stability. An optical microscopy observation showed that the particle morphology and the particle size of the HAPAM emulsion were more regular and bigger than the emulsion without the hydrophobic monomer. The solubility tests showed that such HAPAM w/w emulsions have excellent solubility, which took no more than 180 s to dilute and achieve a homogeneous and clear solution. The rheology measurements showed that the HAPAM association increases with a hydrophobe concentration or the length of hydrophobic alkyl chains, resulting in better shear and temperature resistances. The total reduced viscosity was 124.42 mPa·s for cw101, 69.81 mPa·s for cw6-1, 55.38 mPa·s for cw8-0.25, 48.95 mPa·s for cw12-0.25 and 28 mPa·s for cw16-0.25 when the temperature increased from 30 °C to 90 °C. The cw8-2.0 that contains a 2 mol% hydrophobe monomer has the lowest value at 19.12 mPa·s due to the best association. Based on the excellent stability, solubility and rheological properties, we believe that these HAPAM w/w emulsions could find widespread applications.