Hydrophilic Surface Modification of Amorphous Hydrogenated Carbon Nanocomposite Films via Atmospheric Oxygen Plasma...

Herein we investigated hydrophilic surface modification of SiO_x containing amorphous hydrogenated carbon nanocomposite films (DLC:SiO_x) via the use of atmospheric oxygen plasma treatment. The modified films exhibited effective hydrophilic properties with complete surface wetting. More detailed water droplet contact angle (CA) measurements revealed that oxygen plasma treated DLC:SiO_x films maintained good wetting properties with CA of up to 28 ± 1° after 20 days of aging in ambient air at room temperature. This treatment process also increased surface root mean square roughness from 0.27 nm to 1.26 nm. Analysis of the surface chemical states suggested that the hydrophilic behavior of DLC:SiO_x treated with oxygen plasma is attributed to surface enrichment with C-O-C, SiO₂, and Si-Si chemical bonds as well as significant removal of hydrophobic Si-CH_x functional groups. The latter functional groups are prone to restoration and are mainly responsible for the increase in CA with aging. Possible applications of the modified DLC:SiO_x nanocomposite films could include biocompatible coatings for biomedical applications, antifogging coatings for optical components, and protective coatings to prevent against corrosion and wear.