Repair of Aerospace Composite Structures Using Liquid Thermoplastic Resin

In this study, two types of carbon-fiber-reinforced plastic (CFRP) composite scarf geometries were created using two scarf angles, i.e., 1.43° and 5.71°. The scarf joints were adhesively bonded using a novel liquid thermoplastic resin at two different temperatures. The performance of the repaired laminates was compared with pristine samples in terms of residual flexural strength using four-point bending tests. The repair quality of the laminates was examined by optical micrographs, and the failure modes after flexural tests were analyzed using a scanning electron microscope. The thermal stability of the resin was evaluated by thermogravimetric analysis (TGA), whereas the stiffness of the pristine samples was determined using dynamic mechanical analysis (DMA). The results showed that the laminates were not fully repaired under ambient conditions, and the highest recovery strength at room temperature was only 57% of the total strength exhibited by pristine laminates. Increasing the bonding temperature to an optimal repair temperature of 210 °C resulted in a significant improvement in the recovery strength. The best results were achieved for laminates with a higher scarf angle (5.71°). The highest residual flexural strength was recorded as 97% that of the pristine sample repaired at 210 °C with a scarf angle of 5.71°. The SEM micrographs showed that all the repaired samples exhibited delamination as the dominant failure mode, whereas the pristine samples exhibited dominant fiber fracture and fiber pullout failure modes. The residual strength recovered using liquid thermoplastic resin was found to be much higher than that reported for conventional epoxy adhesives.