Nanoreactor of Fe, N Co-Doped Hollow Carbon Spheres for Oxygen Reduction Catalysis

A simple template strategy was applied to prepare a Fe, N co-doped hollow carbon (Fe-NHC) nanoreactor for the oxygen reduction reaction (ORR) by coating Fe nanoparticles (Fe-NPs) with polydopamine (PDA), followed by high temperature pyrolysis and acid-leaching. With this method, Fe-NPs were used as both the template and the metal precursor, so that the nanoreactors can preserve the original spherical morphology and embed Fe single atoms on the inner walls. The carbonized PDA contained abundant N content, offering an ideal coordination environment for Fe atoms. By regulating the mass ratio of Fe-NPs and PDA, an optimal sample with a carbon layer thickness of 12 nm (Fe-NHC-3) was obtained. The hollow spherical structure of the nanoreactors and the atomically dispersed Fe were verified by various physical characterizations. As a result, Fe-NHC-3 performed well in ORR tests under alkaline conditions, with high catalytic activity, durability, and methanol resistance, demonstrating that the as-fabricated materials have the potential to be applied in the cathodic catalysis of fuel cells.