Thermo-desorption measurements during N-doped Ge-rich Ge₂Sb₂Te₅crystallization

Ge-rich Ge₂Sb₂Te₅(GGST) is considered as one of the best candidates for industrial phase change memory production. GGST memory cells are generally embedded with Si or Ti nitride layers to prevent oxidation, as it leads to an undesired decrease of the GGST crystallization temperature. Furthermore, GGST films are usually doped with elements such as N, C, O, or Bi, aiming to delay GGST crystallization during the fabrication process as well as during memory cell operation. In this work, ultrahigh vacuum thermal desorption spectroscopy (TDS) was performed during isochronal annealing of a N-doped GGST film covered by a 10 nm-thick TiNlayer. Desorption is observed before GGST crystallization, but the comparison between TDS andin situx-ray diffraction measurements shows that the main desorption peak, observed between 653 K and 703 K, occurs after GGST full crystallization. The most prominent desorbing species are Ar, N₂, H₂, and H. These results show that the TiNpolycrystalline layer cannot prevent N atoms from leaving the GGST layer during annealing, suggesting a progressive change of the N-doped GGST chemical composition during thermal annealing and crystallization.