The Effect of Ti Particles Addition on the Microstructure and Mechanical Behavior of Mg AZ31/Al 6082 Composite Sheets

In this study, Ti particles reinforced Mg AZ31/Al 6082 composite sheets were successfully prepared by hot rolling, with the aim of revealing the effect of Ti particles addition on the mechanical behavior and microstructure of Mg AZ31/Al 6082 composite sheets. The results showed that Ti particles were uniformly distributed at the interface of the Mg/Al-Ti composite sheets, which could greatly reduce the amount of Mg-Al intermetallic compounds during annealing treatment. Compared to the Mg/Al sheet, the tensile strength and elongation of the Mg/Al-Ti sheet could be improved simultaneously after the annealing treatment. Ti particles addition hardly affected the grain size, texture type, and tensile fracture morphology of the Mg layer and Al layer in the composite sheets before and after annealing. This present study provides a new perspective on the mechanical behavior and microstructure of Mg/Al composites through the addition of metal particles.