Hydrothermal Synthesis of CaAl-LDH Intercalating with Eugenol and Its Corrosion Protection Performances for Reinforcing Bar

Layered double hydroxides (LDHs) intercalating with a corrosion inhibitor for slowing down the corrosion of a reinforcing bar has attracted considerable attention. However, achieving high-loading capacity of organic inhibitor in LDH with high efficiency and long-term protection characteristics remains an important challenge. In this work, the CaAl-LDH intercalating with eugenol (EG) was synthesized via a continuous hydrothermal method. The prepared LDHs were characterized by SEM, XRD, UV-vis absorption spectra and TGA. Additionally, the corrosion protection performances of LDH-EG for steel bar were studied in detail via the electrochemical method. The results show that the loading amount of EG in LDHs was about 30% and about 80% EG could be released from LDH-EG within 4 h in SCPs containing 3.5% NaCl. The electrochemical test results show that the R value (10⁵~10⁶ Ω · cm²) of steel-mortar incorporated with LDH-EG has increased by 3-4 orders of magnitude compared to the specimen without LDHs (10²~10³ Ω · cm²) after 16 dry-wet cycles corrosion test. The significantly improved protection capability is mainly derived from two aspects: one is the filling effect of LDH, which can fill the pores of mortar and improve the impermeability; another reason is that the intercalated EG can slowly diffuse out of the inner structure of LDHs in a controllable way and result in a relatively long-term effect of corrosion inhibition.