Non-Noble FeCrO Bimetallic Nanoparticles for Efficient NH₃ Decomposition

Ammonia has the advantages of being easy to liquefy, easy to store, and having a high hydrogen content of 17.3 wt%, which can be produced without CO through an ammonia decomposition using an appropriate catalyst. In this paper, a series of FeCr bimetallic oxide nanocatalysts with a uniform morphology and regulated composition were synthesized by the urea two-step hydrolysis method, which exhibited the high-performance decomposition of ammonia. The effects of different FeCr metal ratios on the catalyst particle size, morphology, and crystal phase were investigated. The Fe_0.75Cr_0.25 sample exhibited the highest catalytic activity, with an ammonia conversion of nearly 100% at 650 °C. The dual metal catalysts clearly outperformed the single metal samples in terms of their catalytic performance. Besides XRD, XPS, and SEM being used as the means of the conventional characterization, the local structural changes of the FeCr metal oxide catalysts in the catalytic ammonia decomposition were investigated by XAFS. It was determined that the Fe metal and FeN of the bcc structure were the active species of the ammonia-decomposing catalyst. The addition of Cr successfully prevented the Fe from sintering at high temperatures, which is more favorable for the formation of stable metal nitrides, promoting the continuous decomposition of ammonia and improving the decomposition activity of the ammonia. This work reveals the internal relationship between the phase and structural changes and their catalytic activity, identifies the active catalytic phase, thus guiding the design and synthesis of catalysts for ammonia decomposition, and excavates the application value of transition-metal-based nanocomposites in industrial catalysis.