Environment-friendly, efficient process for mechanical recovery of waste lithium iron phosphate batteries

Technology for recycling retired lithium batteries has become increasingly environment-friendly and efficient. In traditional recovery methods, pyrometallurgy or hydrometallurgy is often used as an auxiliary treatment method, which results in secondary pollution and increases the cost of harmless treatment. In this article, a new method for combined mechanical recycling of waste lithium iron phosphate (LFP) batteries is proposed to realize the classification and recycling of materials. Appearance inspections and performance tests were conducted on 1000 retired LFP batteries. After discharging and disassembling the defective batteries, the physical structure of the cathode binder was destroyed under ball-milling cycle stress, and the electrode material and metal foil were separated using ultrasonic cleaning technology. After treating the anode sheet with 100 W of ultrasonic power for 2 minutes, the anode material was completely stripped from the copper foil, and no cross-contamination between the copper foil and graphite was observed. After the cathode plate was ball-milled for 60 seconds with an abrasive particle size of 20 mm and then ultrasonically treated for 20 minutes with a power of 300 W, the stripping rate of the cathode material reached 99.0%, and the purities of the aluminium foil and LFP reached 100% and 98.1%, respectively.