A novel glass ionomer cement with silver zeolite for restorative dentistry

To develop an antimicrobial silver zeolite glass ionomer cement (SZ-GIC) and determine its biocompatibility, physical, adhesive and antibacterial properties.

Silver nitrate and sodium zeolite were used to synthesize silver zeolite (SZ). SZ-GICs were prepared by incorporating SZ into GIC at 5% (SZ-GIC5), 2% (SZ-GIC2), or 1% (SZ-GIC1) by weight, respectively. The SZ-GICs were characterized by evaluating surface morphology, topography and elemental composition. SZ-GICs' biocompatibility was assessed by evaluating cell cytotoxicity. Their physical properties were determined by testing setting time, compressive strength, flexural strength, water sorption and solubility. Their adhesive property was assessed by evaluating micro-tensile bond strength. Their antibacterial properties were assessed by evaluating biofilm growth kinetic, metabolic activity, viability and morphology. GIC was used as a control.

SZ was a three-dimensional crystalline mineral. SZ-GICs (including SZ-GIC 5, 2 and 1) showed similar surface morphology and topography to GIC. SZ-GIC1 and GIC had no difference in cell cytotoxicity (p>0.05). SZ-GICs and GIC showed no difference in setting time (p>0.05). SZ-GICs had higher compressive and flexural strength than GIC (p<0.05). SZ-GIC2 and SZ-GIC1 showed lower water sorption and solubility than GIC (p<0.05). SZ-GICs had higher micro-tensile bond strength than GIC (p<0.05). Biofilms on SZ-GICs' surfaces showed lower colony-forming units, decreased metabolic activities, higher percentages of dead cells and more ruptured bacterial cells compared with those on GIC.

SZ-GIC with silver zeolite at 1% by weight are as biocompatible as conventional GIC. The SZ-GICs have enhanced physical, adhesive and antibacterial properties than GIC.

A silver zeolite glass ionomer cement was developed. The SZ-GICs have great potential for caries prevention and management.