Modified gelatin hydrogel nonwoven fabrics (Genocel) as a skin substitute in murine skin defects

From previous research, an emerging material composed of gelatin hydrogel nonwoven fabric (Genocel) has shown potential as a skin substitute, by improving neovascularization promotion in the early phase of wound healing. However, Genocel was inferior in terms of granulation formation compared to Pelnac. To solve this problem, we modified the manufacturing process of Genocel to reduce its water content, extend the degradation time (Genocel-L), and evaluate its healing process as a skin substitute.

Genocel with a low water content (Genocel-L) was prepared and the difference in water content compared to that of the conventional Genocel was confirmed. Degradation tests were performed using collagenase and compared among Genocel-L, Genocel, and Pelnac sheets. In the in vivo study, sheets of Genocel-L or Pelnac were applied to skin defects created on the backs of C57BL/6JJcl mice. On days 7, 14, and 21, the remaining wound area was evaluated and specimens were harvested for Hematoxylin and Eosin, Azan, anti-CD31, CD68, and CD163 staining to assess neoepithelialization, granulation tissue, capillary formation, and macrophage infiltration.

Genocel-L had a lower water content than the conventional Genocel and a slower degradation than Genocel and Pelnac. In the in vivo experiment, no significant differences were observed between Genocel-L and Pelnac in relation to the wound area, neoepithelium length, granulation formation, and the number of newly formed capillaries. The area of newly formed capillaries in the Pelnac group was significantly larger than that in the Genocel-L group on day 21 (p < 0.05). Regarding macrophage infiltration, significantly more M2 macrophages were induced in the Pelnac group on days 14 and 21, and the M2 ratio was larger in the Pelnac group (p < 0.05) during the entire process.

Genocel-L has a lower water content and slower degradation rate than the conventional Genocel. Genocel-L had equivalent efficacy as a skin substitute to Pelnac, and can therefore be considered feasible for use as a skin substitute. However, a manufacturing method that can further modify Genocel-L is required to recover its early angiogenic potential.