Osteogenic differentiation of human adipose-derived mesenchymal stem cells in a bisphosphonate-functionalized...

Recent trends in bone tissue engineering have focused on the development of biomimetic constructs with appropriate mechanical and physiochemical properties. Here, we report the fabrication of an innovative biomaterial scaffold based on a new bisphosphonate-containing synthetic polymer combined with gelatin. To this end, zoledronate (ZA)-functionalized polycaprolactone (PCL-ZA) was synthesized by a chemical grafting reaction. After adding gelatin to the PCL-ZA polymer solution, the porous PCL-ZA/gelatin scaffold was fabricated by the freeze-casting method. A scaffold with aligned pores and a porosity of 82.04 % was obtained. During in vitro biodegradability test, 49 % of its initial weight lost after 5 weeks. The elastic modulus of the PCL-ZA/gelatin scaffold was 31.4 MPa, and its tensile strength was 4.2 MPa. Based on the results of MTT assay, the scaffold had good cytocompatibility with human Adipose-Derived Mesenchymal Stem Cells (hADMSCs). Furthermore, cells grown in PCL-ZA/gelatin scaffold showed the highest mineralization and ALP activity compared to other test groups. Results of the RT-PCR test revealed that RUNX2, COL 1A1, and OCN genes were expressed in PCL-ZA/gelatin scaffold at the highest level, suggesting its good osteoinductive capacity. These results revealed that PCL-ZA/gelatin scaffold could be considered a proper biomimetic platform for bone tissue engineering.