In-situ magnetite deposited wood composites with extensive electromagnetic interference shielding performance

Wood is an insulator material, using its porous structure to endow it with efficient microwave absorption and broaden its application range is still a major challenge. Here, wood-based Fe₃O₄ composites with excellent microwave absorption properties and high mechanical strength were prepared by alkaline sulfite method, in-situ co-precipitation method and compression densification method. The results showed that the magnetic Fe₃O₄ was densely deposited in the wood cells, and the prepared wood-based microwave absorption composites had both high electrical conductivity, magnetic loss, excellent impedance matching performance and attenuation performance, as well as effective microwave absorption properties. In the frequency range of 2-18 GHz, the minimum reflection loss value was -25.32 dB. At the same time, it had high mechanical properties. Compared with the untreated wood, its modulus of elasticity (MOE) in bending increased by 98.77%, and modulus of rapture (MOR) in bending improved by 67.9%. The developed wood-based microwave absorption composite is expected to be used in electromagnetic shielding fields such as anti-radiation and anti-interference.