Energy Alignment of Quantum-Confined ZnO Particles with Copper Oxides for Heterojunctions with Improved...

The ability to control electronic states by utilizing quantum confinement of one of the material components in heterojunctions is a promising approach to perform energy-level matching. In this work, we report the possibility to achieve optimum energy alignment in heterojunctions made from size-controlled quantum dots (Q-dots) of ZnO in combination with three copper oxides: Cu₂O, Cu₄O₃, and CuO. Quantum confinement effects on the ZnO nanoparticles in the diameter range 2.6-7.4 nm showed that the direct optical band gap decreased from 3.99 to 3.41 eV, with a dominating shift occurring in the conduction band (CB) edge, and thus the possibility to obtain close to 0.6 eV CB edge shift by controlling the size of ZnO. The effect was utilized to align the electronic bands in the ZnO Q-dot/copper oxide heterojunctions to allow for charge transfer between the materials and to test the ability to improve the photocatalytic performance for the system, evaluated by the transformation of a dye molecule in water. The catalyst materials were investigated by X-ray diffraction, scanning electron microscopy, ultraviolet-visible (UV-vis), photoluminescence, and Raman spectroscopy. The most promising material combination was found to be the Cu₂O copper oxide in combination with an energy aligned ZnO Q-dot system with approximately 7 nm diameter, showing strong synergy effects in good agreement with the energy-level analysis, outperforming the added effect of its individual components, ZnO-Q-dots and Cu₂O, by about 140%. The results show that utilization of a heterojunction with controllable energy alignment can provide a drastically improved photocatalytic performance. Apart from increased photocatalytic activity, specific surface states of ZnO are quenched when the heterojunction is created. It is anticipated that the same approach can be utilized in several material combinations with the added benefit of a system with controllable overpotential and thus added specificity for the targeted reduction reaction.