High bending strength at 1800 °C exceeding 1 GPa in TiB₂-B₄C composite

High density (99.5%) ceramic composite composed of titanium boride and boron carbide (70/30 vol%) was obtained by spark plasma sintering and was tested by 3-point bending test in Ar atmosphere at 1800 °C. Bending strength was high, around 1.1 GPa. The strength-strain curve presents a peculiar shape composed of three regions where elastic and plastic deformations are active with a different weight. Based on transmission electron microscopy observations we propose a process of mechanical energy absorption driven by shear stress in the boron carbide crystals: stacking faults with (1-11) and (011) stacking planes and twins with (1-11) twinning plane rearrange into nano-twins with (10-1) twinning planes, orthogonal but equivalent to the initial ones. This rearrangement mechanism provides in the first instance a plastic signature, but further contributes strengthening.