Gentamicin Sulfate Grafted Magnetic GO Nanohybrids with Excellent Antibacterial Properties and Recyclability

In this study, magnetic graphene oxide (MGO) nanohybrids were first prepared by loading Fe₃O₄ NPs onto graphene oxide (GO). Then, GS-MGO nanohybrids were prepared by grafting gentamicin sulfate (GS) onto MGO directly using a simple amidation reaction. The prepared GS-MGO had the same magnetism as MGO. They exhibited excellent antibacterial ability against Gram-negative bacteria and Gram-positive bacteria. The GS-MGO had excellent antibacterial performance against Escherichia coli (E. coli), Staphylococcus aureus (S. aureus), and Listeria monocytogenes (L. monocytogenes). When the addition concentration of GS-MGO was 1.25 mg/mL, the calculated bacteriostatic ratios against E. coli and S. aureus achieved 89.8% and 100%, respectively. For L. monocytogenes, only 0.05 mg/mL of GS-MGO had an antibacterial ratio as high as 99%. In addition, the prepared GS-MGO nanohybrids also exhibited excellent non-leaching activity with good recycling antibacterial ability. After eight times antibacterial tests, GS-MGO nanohybrids still exhibited an excellent inhibition effect on E. coli, S. aureus, and L. monocytogenes. Therefore, as a non-leaching antibacterial agent, the fabricated GS-MGO nanohybrid had dramatic antibacterial properties and also showed great recycling ability. Thus, it displayed great potential in the design of novel recycling antibacterial agents with non-leaching activity.