Microstructural, biocompatibility and mechanical investigation of MgHAp and AgHAp: Comparative report

It is imperative to investigate the effect of addition of different size metallic ions in HAp and study the changes in biocompatibility and mechanical properties. Silver and magnesium ions are two vital ions needed in our body. Silver ions are known to inhibit the microbes, while magnesium ions are known to increase the mechanical properties. The present study reports the comparative properties of MgHAp and AgHAp synthesised by sol-gel wet chemical method. Changes in the morphology, phase analysis, corrosion resistance, dielectric properties, hardness and the thrombus behaviour of HAp doped Ag and Mg ions has been investigated. In this work, we have presented a comparative study of both the metal doped ionsto find which of the ions and which weight percent of the ions can be best suited to be incorporated into the HAp matrix for hard tissue implants. All wt% AgHAp showed the better corrosion resistance than all the MgHAp samples. However, MgHAp showed higher value of hardness in comparison to AgHAp samples. The mechanical strength was found to increase with the increase in Mg wt% in MgHAp but for AgHAp the hardness value decreased with increase in the concentration. The impedance and dielectric loss decreased with increasing frequency for both the samples. Both the ion doped hydroxyapatite showed moderate clotting behaviour as compared to pure HAp. But 2 wt% MgHAp and 4 wt% AgHAp showed better thrombogenic behaviour. It is imperative to investigate the effect of addition of different size metallic ions in HAp and study the changes in biocompatibility and mechanical properties. Silver and magnesium ions are two vital ions needed in our body. Silver ions are known to inhibit the microbes, while magnesium ions are known to increase the mechanical properties. The present study reports the comparative properties of MgHAp and AgHAp synthesised by sol-gel wet chemical method. Changes in the morphology, phase analysis, corrosion resistance, dielectric properties, hardness and the thrombus behaviour of HAp doped Ag and Mg ions has been investigated. In this work we have presented a comparative study of both the metal doped ions to find which of the ions and which weight percent of the ions can be best suited to be incorporated into the HAp matrix for hard tissue implants. All wt% AgHAp showed the better corrosion resistance than all the MgHAp samples. However, MgHAp showed higher value of hardness in comparison to AgHAp samples. The mechanical strength was found to increase with the increase in Mg wt% in MgHAp but for AgHAp the hardness value decreased with increase in the concentration. The impedance and dielectric loss decreased with increasing frequency for both the samples. Both the ion doped hydroxyapatite showed moderate clotting behaviour as compared to pure HAp. But 2 wt% MgHAp and 4 wt% AgHAp showed better thrombogenic behaviour.